Material response and failure mechanism of unidirectional metal matrix composites under impulsive shear loading

The material response and failure mechanism of unidirectional metal matrix composite under impulsive shear loading are investigated in this paper. Both experimental and analytical studies were performed. The shear strength of unidirectional C-f/A356.0 composite and A356.0 aluminum alloy at high strain rate were measured with a modified split Hopkinson torsional bar technique. The results indicated that the carbon fibers did not improve the shear strength of aluminum matrix if the fiber orientation aligned with the shear loading axis. The microscopic inspection of the fractured surface showed a multi-scale zigzag feature which implied a complicated shear failure mechanism in the composite. In addition to testing, the micromechanical stress field in the composite was analyzed by the generalized Eshelby equivalent method (GEEM). The influence of cracking in matrix on the micromechanical stress field was investigated as well. The results showed that the stress distribution in the composite is quite nonhomogeneous and very high shear stress concentrations are found in some regions in the matrix. The high shear stress concentration in the matrix induces tensile cracking at 45 degrees to the shear direction. This in turn aggravates the stress concentration at the fiber/matrix interface and finally leads to a catastrophic failure in the composite. From the correlation between the analysis and experimental results, the shear failure mechanism of unidirectional C-f/A356.0 composite can be elucidated qualitatively.

Molecular dynamics simulation of hydrogen enhancing dislocation emission

The interactive pair potential between Al and H is obtained based on the ab initio calculation and the Chen-Mobius 3D lattice inversion formula. By utilizing the pair potentials calculated, the effects of hydrogen on the dislocation emission from crack tip have been studied. The simulated result shows that hydrogen can reduce the cohesive strength for Al single crystal, and then the critical stress intensity factor for partial dislocation emission decreases from 0.11 MPa root m (C-H = 0) to 0.075 MPa root m (C-H=0.72%) and 0.06 MPa root m (C-H = 1.44%). This indicates thar hydrogen can enhance the dislocation emission. The simulation also shows that atoms of hydrogen can gather and turn into small bubbles, resulting in enhancement of the equilibrium vacancy concentration.

Dynamic function of damage and its implications

Dynamic function of damage is the key to the problem of damage evolution of solids. In order to understand it, one must understand its mesoscopic mechanisms and macroscopic formulation. In terms of evolution equation of microdamage and damage moment, a dynamic function of damage is strictly defined. The mesoscopic mechanism underlying self-closed damage evolution law is investigated by means of double damage moments. Numerical results of damage evolution demonstrate some common features for various microdamage dynamics. Then, the dynamic function of damage is applied to inhomogeneous damage field. In this case, damage evolution rate is no longer equal to the dynamic function of damage. It is found that the criterion for damage localization is closely related to compound damage. Finally, an inversion of damage evolution to the dynamic function of damage is proposed.

Some advances in study of crack identification problems

In the present paper, the crack identification problems are investigated. This kind of problems belong to the scope of inverse problems and are usually ill-posed on their solutions. The paper includes two parts: (1) Based on the dynamic BIEM and the optimization method and using the measured dynamic information on outer boundary, the identification of crack in a finite domain is investigated and a method for choosing the high sensitive frequency region is proposed successfully to improve the precision. (2) Based on 3-D static BIEM and hypersingular integral equation theory, the penny crack identification in a finite body is reduced to an optimization problem. The investigation gives us some initial understanding on the 3-D inverse problems.

Propagation of Explosion Wave in Hard-Soft-Hard Layered Media

The paper presents a reasonable analysis for dynamic response and failure process of a plane multi-layered media, which are subjected to a blast loading. This blast loading is induced by a cylindric explosive put on the center of top surface of the layered media. With the help of numerical simulation technique provided by LS-DYNA software, the whole process of explosion wave propagation and attenuation can be revealed. The feature of local failure around the blasting site is also discussed in some detail. Our focus will be on the explosion wave attenuation for the hard-soft-hard sandwich layers. As seen in the paper, the computational results are delivered in a feasible way by comparing with experimental data.

Torsion fracture behavior of drawn pearlitic steel wires with different heat treatments

In this paper, torsion fracture behavior of drawn pearlitic steel wires with different heat treatments was investigated. Samples with different heat treatments was investigated. Samples with different heat treatment conditions were subjected to torsion and tensile tests. The shear strain along the torsion sample after fracture was measured. Fracture surface of wires was examined by Scanning Electron Microscopy. In addition, the method of Differential Scanning Calorimetry was used to characterize the thermodynamic process in the heat treatment. A numerical simulation via finite element method on temperature field evolution for the wire during heat treatment process was performed. The results show that both strain aging and recovery process occur in the material within the temperature range between room temperature and 435 degrees C. It was shown that the ductility measured by the number of twists drops at short heating times and recovers after further heating in the lead bath of 435 degrees C. On the other hand, the strenght of the wire increases at short heating times and decreases after further heating. The microstructure inhomogeneity due to short period of heat treatment, coupled with the gradient characteristics of shear deformation during torsion results in localized shear deformation of the wire. In this situation, shear cracks nucleate between lamella and the wire breaks with low number of twists.

Subsonic interface crack with crack face contact

A steady-state subsonic interface crack propagating between an elastic solid and a rigid substrate with crack face contact is studied. Two cases with respective to the contact length are considered, i.e., semi-infinite and finite crack face contact. Different from a stationary or an open subsonic interface crack, stress singularity at the crack tip in the present paper is found to be non-oscillatory. Furthermore, in the semi-infinite contact case, the singularity of the stress field near the crack tip is less than 1/2. In the finite contact case, no singularity exists near the crack tip, but less than 1/2 singularity does at the end of the contact zone. In both cases, the singularity depends on the linear contact coefficient and the crack speed. Asymptotic solutions near the crack tip are given and analyzed. In order to satisfy the contact conditions, reasonable region of the linear contact coefficient is found. In addition, the solution predicts a non-zero-energy dissipation rate due to crack face contact.

Interface cracking and particulate size effect in particle-reinforced metal-matrix composites

The mechanical behaviors of the ceramic particle-reinforced metal matrix composites are modeled based on the conventional theory of mechanism-based strain gradient plasticity presented by Huang et al. Two cases of interface features with and without the effects of interface cracking will be analyzed, respectively. Through comparing the result based on the interface cracking model with experimental result, the effectiveness of the present model can be evaluated. Simultaneously, the length parameters included in the strain gradient plasticity theory can be obtained.

Study on fatigue crack nucleation of electrodeposited nanocrystalline nickel

The mechanism of fatigue crack nucleation for nanocrystalline (nc) nickel was experimentally investigated in this paper. The samples of electrodeposited ne nickel were loaded cyclically by using a three point bending instrument at first. Then, atomic force microscopy (AFM) was used to scanning the sample surface after fatigue testing. The results indicated that, after fatigue testing, there are vortex-like cells with an average size of 108nm appeared along the crack on nc nickel sample. And, the roughness of sample surface increased with the maximum stress at the surface.

Flow similariy applied in convection-based tilt sensor

The environment temperature has inevitable effects on property of the convect ion-based tilt sensors. It not only redefines the application, but also prevents the improvement of the sensor performance. Numerical simulation of the fluid flow in the chamber of a sensor was performed and the influence of the environment temperature was studied in this paper. At zero tilt angle, the temperature distribution along the perpendicular line cross the heat source at various environment temperatures was presented. It was found that the flow varied dramatically at different environment temperatures, which would cause the output signal vary accordingly, even when the tilt angle was kept at a constant, because this device works by sensing the change of flow. At the same condition, we present the numerical results when the temperature difference across the heat source and the environment was kept at the same, in those results, it was found that the temperature difference at every point along the perpendicular line cross the heat source keep the same, this result confirms the similarity principle of nature convection. Second, A method of eliminating environment temperature infect on property of convect ion-based tilt sensor, which is based on the theory of flow similarity, is proposed. It was found that a thermal transistance can be piped on the circuit of heat source to compensate the temperature of the heat source. A compensative circuit was specially designed which can keep flow similarity by changing heat source temperature in order to eliminate the influence of environment temperature. The experiment results show that above 70% temperature drift can be eliminated by this compensative circuit.

四膜虫:毒理学与生态毒理学研究中的优良模式生物

四膜虫 (Tetrahymena)是毒理学与生态毒理学研究的良好模式生物之一。本文回顾了近年来以四膜虫为实验生物开展的毒理学与生态毒理学研究进展 ,并针对目前产生严重环境压力的持久性有毒化学污染物 ,提出了以四膜虫为模式生物开展相应的生态毒理学研究的前景以及可行的方法。

Low threshold current density 1.5 mu m strained-MQW laser by n-type modulation-doping

1.5 mu m. n-type modulation-doping InGaAsP/InGaAsP strained multiple quantum wells grown by low pressure metalorganic chemistry vapor decomposition technology is reported for the first time in the world. N-type modulation-doped lasers exhibit much lower threshold current densities than conventional lasers with undoped barrier layers. The lowest threshold current density we obtained was 1052.5 A/cm(2) for 1000 mu m long lasers with seven quantum wells. The estimated threshold current density for an infinite cavity length was 94.72A/cm(2)/well, reduced by 23.3% compared with undoped barrier lasers. The n-type modulation doping effects on the lasing characteristics in 1.5 mu m devices have been demonstrated.

Silica and alumina thin films grown by liquid phase deposition

This work demonstrates the condition optimization during liquid phase deposition (LPD) Of SiO2/GaAs films. LPD method is further applied to form Al2O3 films on semiconductors with poison-free materials. Proceeding at room temperature with inexpensive equipment, LPD of silica and alumina films is potentially serviceable in microelectronics and related spheres.

Interface-related in-plane optical anisotropy of quantum wells studied by reflectance-difference spectroscopy

The in-plane optical anisotropy of three groups of GaAs/AlGaAs quantum well structures has been studied by reflectance-difference spectroscopy (RDS). For GaAs/Al0.36Ga0.64As single QW structures, it is found that the optical anisotropy increases quickly as the well width is decreased. For an Al0.02Ga0.98As/AlAs multiple QW with a well width of 20nm, the optical anisotropy is observed not only for the transitions between ground states but also for those between the excited states with transition index n up to 5. An increase of the anisotropy with the transition energy, or equivalently the transition index n, is clearly observed. The detailed analysis shows that the observed anisotropy arises from the interface asymmetry of QWs, which is introduced by atomic segregation or anisotropic interface roughness formed during the growth of the structures. More, when the 1 ML InAs is inserted at one interface of GaAs/AlGaAs QW, the optical anisotropy of the QW can be increased by a factor of 8 due to the enhanced asymmetry of the QW. These results demonstrate clearly that the RDS is a sensitive and powerful tool for the characterization of semiconductor interfaces.

Controlled growth of III-V compound semiconductor nano-structures and their application in quantum-devices

This paper reviews our work on controlled growth of self-assembled semiconductor nanostructures, and their application in light-emission devices. High-power, long-life quantum dots (QD) lasers emitting at similar to 1 mu m, red-emitting QD lasers, and long-wavelength QD lasers on GaAs substrates have successfully been achieved by optimizing the growth conditions of QDs.